Transparent Moulded Part PVC Compound

Get a Price/Quote

MOQ : 10 Pieces

Transparent Moulded Part PVC Compound Specification

Material
PVC

Temperature
-10C to 70C

Smell
Odorless

CAS No
9002-86-2

HS Code
390410

Harness
Medium to High

Processing
Injection Molding, Extrusion

Type
Transparent Moulded Part PVC Compound

Appearance
Clear

Color
Brown

Shape
Other

Relative Density
1.20 - 1.35

Shore Hardness
96%

Tensile Strength(Mpa)
10-15 MPa

Elongation(%)
200 - 350%

Heat Stability
Good

Storage Condition
Cool and dry place

Applications
Medical, Automotive, General Industrial

Transparency
High

Chemical Resistance
Resistant to acids, bases, and oils

Weather Resistance
Excellent

Electrical Insulation
Excellent

Impact Strength
High

Water Absorption
<0.1%

Flame Retardancy
Optional

Transparent Moulded Part PVC Compound Trade Information

Minimum Order Quantity
10 Pieces

Supply Ability
500 Pieces Per Week

Delivery Time
2-3 Days

Main Domestic Market
All India

About Transparent Moulded Part PVC Compound

Having immense experience of more than five decades in this domain, we are successfully engaged in offering quality assured Transparent Moulded Part PVC Compound. It is processed using top notch quality polyvinyl chloride and modern methodology with the help of dexterous professionals. Owing to its impurity free composition, the provided product is convenient for manufacturing transparent molded parts of machines, automobiles and medical equipment. Moreover, the offered Transparent Moulded Part PVC Compound is accessible from us at the most economical prices.

Key points:

Longer shelf life
Flame retardant
Precise composition
High clarity attribute

TECHNICAL DATA SHEET

Polyvinyl Chloride Compound
ER 315 GT is a high flow, medium impact, transparent compound ideally suited for variety of clear moulded components.

PROPERTIES	STANDARD	UNIT	TYPICAL VALUE
PHYSICAL
Appearance			Granular
Specific Gravity	ASTM D 792		1.32 Â± 0.03
MECHANICAL
Hardness	ASTM D 2240	Shore D	73 + 3
Tensile Strength (min.)	ASTM D 638	MPa	60
Elongation at Break (min.)	ASTM D 638	%	18
Izod impact, notched 80x10x4 (23 Â°C) (min.)	ASTM D 256	KJ/M²	10
Flexural Modulus, 2 mm/min (min.)	ISO 178	MPa	2400
THERMAL
HDT/Be, 0.45 MPa edgew 120x10x4/s=100 mm	ASTM D 648	^oC	60
Co efficient of linear thermal expansion	ISO 11359-2	%	8.1 x 10^-5
RHEOLOGICAL
MVR (min.) (210^oC/20 Kg)	ASTM D 1238	cc /10 min	20
FLAMMABILITY
94V-0 Flame Class rating	UL 94	mm	1.00
Glow wire Test, 850^oC, Passes a	IEC 60695-2-12	mm	1.0
PROCESSING INFORMATION
Temperature Range		^oC	165-180
Mould Shrinkage		cm/cm	0.045