Modular Switch Plate PVC Compound

Get a Price/Quote

MOQ : 10 Pieces

Modular Switch Plate PVC Compound Specification

Smell
Odorless

Material
PVC

Processing
Injection Molding

Temperature
-10C to +70C

CAS No
9002-86-2

HS Code
39269099

Harness
High Rigidity

Type
Modular Switch Plate PVC Compound

Appearance
Smooth, Glossy Finish

Color
Brown

Shape
Other

Relative Density
1.4 g/cm3 - 1.6 g/cm3

Shore Hardness
98%

Tensile Strength(Mpa)
15 MPa

Elongation(%)
130%

Heat Stability
30 Min at 180C

Insulation Resistance
> 10^12 cm

Electrical Strength
> 25 kV/mm

Flame Retardancy
Self-Extinguishing

Toxicity
Non-toxic, Lead Free

Weather Resistance
Good UV Stability

Chloride Content
57% by weight

Impact Strength
High

Application
Electrical Switch Covers & Plates

Moisture Absorption
< 0.1%

Packaging Size
Customized as per requirement

RoHS Compliance
Yes

Surface Finish
Matte/Glossy Available

Modular Switch Plate PVC Compound Trade Information

Minimum Order Quantity
10 Pieces

Supply Ability
500 Pieces Per Week

Delivery Time
2-3 Days

Main Domestic Market
All India

About Modular Switch Plate PVC Compound

We have started our business by manufacturing, exporting and supplying quality approved Modular Switch Plate PVC Compound. Extensively demanded in electrical and electronic industry, the offered product is utilized by customers for manufacturing switch plates. We provide this product to the clients in moisture proof packaging options at the most competitive prices. With the aid of our knowledgeable professionals, this Modular Switch Plate PVC Compound is processed using top notch quality polyvinyl chloride and sophisticated methodology.

Key points:

Optimum shelf life
Safe to use
Free from impurities
Emits less smoke

TECHNICAL DATA SHEET

Polyvinyl Chloride Compound
ER 315 GT is a high flow, medium impact, transparent compound ideally suited for variety of clear moulded components.

PROPERTIES	STANDARD	UNIT	TYPICAL VALUE
PHYSICAL
Appearance			Granular
Specific Gravity	ASTM D 792		1.22 Â± 0.03
MECHANICAL
Hardness	ASTM D 2240	Shore D	73 + 3
Tensile Strength (min.)	ASTM D 638	MPa	60
Elongation at Break (min.)	ASTM D 638	%	18
Izod impact, notched 80x10x4 (23 ^oC) (min.)	ASTM D 256	KJ/M²	10
Flexural Modulus, 2 mm/min (min.)	ISO 178	MPa	2400
THERMAL
HDT/Be, 0.45 MPa edgew 120x10x4/s=100 mm	ASTM D 648	^oC	60
Co efficient of linear thermal expansion	ISO 11359-2	%	8.1 x 10^-5
RHEOLOGICAL
MVR (min.) (210^oC/20 Kg)	ASTM D 1238	cc /10 min	20
FLAMMABILITY
94V-0 Flame Class rating	UL 94	mm	1.00
Glow wire Test, 850^oC, Passes a	IEC 60695-2-12	mm	1.0
PROCESSING INFORMATION
Temperature Range		^oC	155-165
Mould Shrinkage		cm/cm	0.045