Flame Retardant Sheathing PVC Compound

Get a Price/Quote

MOQ : 10 Pieces

Flame Retardant Sheathing PVC Compound Specification

Harness
Medium

Processing
Suitable for extrusion, injection molding

Smell
Odorless

HS Code
390410

Material
PVC

CAS No
9002-86-2

Temperature
-15C to 70C service range

Type
Flame Retardant Sheathing PVC Compound

Appearance
Uniform green pellets

Color
Brown

Shape
Other

Relative Density
1.45 - 1.55 g/cm3

Shore Hardness
98%

Tensile Strength(Mpa)
13 MPa

Elongation(%)
200%

Heat Stability
80 minutes (at 180C)

Processing Temperature
150C - 180C

Flame Retardant Standard
Meets UL-94 V-0

Oxygen Index
30%

Application
Wire & cable sheathing for electrical insulation

Water Absorption
0.1%

Packaging
25kg bag

Compatibility
Optimized for cable sheathing applications

Volume Resistivity
> 1.0 1014 cm

Storage
Store in cool, dry place, away from direct sunlight

Flame Retardant Sheathing PVC Compound Trade Information

Minimum Order Quantity
10 Pieces

Supply Ability
500 Pieces Per Week

Delivery Time
2-3 Days

Main Domestic Market
All India

About Flame Retardant Sheathing PVC Compound

We are recognized as profound entity in this domain, betrothed in offering superior quality Flame Retardant Sheathing PVC Compound. Under the guidance of our ingenious professionals, this product is processed by utilizing premium grade polyvinyl chloride and innovative methodology. Owing to its ability to emit less and resistant frame, the provided product is used for coating of wires. Clients can purchase the offered Flame Retardant Sheathing PVC Compound from us at pocket friendly prices within promised time frame.

Key points:

Free from impurities
Safe to use
Anti-aging property
Longer shelf life

TECHNICAL DATA SHEET

Polyvinyl Chloride Compound
SFR 90 is a FR compound designed to be used for Flame Retardant Insulation application.

PROPERTIES	STANDARD	UNIT	TYPICAL VALUE
PHYSICAL
Appearance			Granular
Specific Gravity	ASTM D 792		1.52 Â± 0.03
MECHANICAL
Hardness	ASTM D 2240	Shore A	90 Â± 3
Tensile Strength (min.)	IS 10810	MPa	15
Elongation at Break (min.)	IS 10810	%	200
Properties after ageing at 80^oC for 7 days
Variation in Tensile Strength	IS 10810	%	+ 20
Variation in Elongation at Break	IS 10810	%	+ 20
Loss of Mass	IS 10810	mg/cm²	2 (max.)
THERMAL
Thermal Stability @ 200^oC (min.)	IS 5831	Minutes	80
ELECTRICAL
Volume Resistivity (min.)	ASTM D 257	Ohm.cm	5 x 10¹³
FLAMMABILITY
Limiting Oxygen Index (min.)	ASTM D 2863	%	30
Temperature Index (min.)	ASTM D 2863	^oC	250
PROCESSING INFORMATION
Temperature Range		^oC	160â€“180